Catalyst composition with support comprising titanium oxide and clay mineral for vapor phase reduction of nitrogen oxides

ABSTRACT

A catalyst composition for the vapor phase reduction of nitrogen oxides with ammonia, which consists essentially of a non-noble transition metal compound supported on a shaped carrier comprising a titanium oxide and a clay mineral having an average particle size of 0.1 to 100 microns. The shaped carrier preferably contains an additional component which is an inorganic fibrous material, silica hydrogel, silica sol, or a mixture of at least two of these. An exhaust gas containing nitrogen oxides is treated, with a high percent NO removal, by contacting it with the catalyst composition in the presence of ammonia gas at 200 to 600° C.

This invention relates to a process for the catalytic vapor phasereduction of nitrogen oxides to nitrogen and water, and to an improvedcatalyst composition which retains high catalytic activity stably overlong periods of time, has superior strength that can withstand adestructive force exerted during its handling and use, and can catalyzethe reduction of nitrogen oxides contained in waste and exhaust gases toharmless nitrogen and water with marked industrial advantage.

The catalyst composition of the invention retains its high catalyticactivity and superior resistance to poisoning for long periods of timein the reduction of nitrogen oxides. It has moldability into any desiredshape. The molded catalyst composition has high physical strengthsufficient to withstand the physical destructive force exerted on itduring its handling and transportation, and its use in variousoperations such as charging into a reducing zone or reducing treatment.The catalyst composition also permits the decrease of pressure drop andmaintains a low pressure drop over long periods. Moreover, the low costof the catalyst composition adds to the industrial advantages of theprocess of this invention.

Nitrogen oxides (mainly denoting NO and NO₂ ; generically called"nitrogen oxides" in the present application) are contained in waste andexhaust gases of various sources, such as boiler exhausts and motorvehicle exhausts. They are toxic to the humans, and are considered to besubstances which will cause air pollution in the form of, say,photo-chemical smog, affecting not only the workers of industrialestablishments but also the general public. This is a serious socialproblem, and needs to be solved by exploiting effective measures forremoving nitrogen oxides from various exhaust and waste gases orconverting them to harmless compounds.

A number of methods have heretofore been suggested in an attempt to meetthis need. These prior methods can be divided roughly into a wetabsorbing process by which nitrogen oxides are removed by causing themto be absorbed by, for example, an alkali aqueous solution or an aqueoussolution of a bisulfite, and a dry catalytic reduction process by whichnitrogen oxides are reduced using a catalyst. Of these methods, agas-phase catalytic reduction method using ammonia is currentlyconsidered to be most advantageous for commercial operations. Thepresent invention relates to a process for the vapor phase catalyticreduction of nitrogen oxides by this type of process, and to a catalystcomposition used for it.

Reduction of nitrogen oxides by this type of process is performed bycontacting an exhaust gas containing the nitrogen oxides with an ammoniagas at elevated temperatures in the presence of a catalyst, thereby toreduce the nitrogen oxides to harmless nitrogen and water, asschematically shown below.

    6NO + 4NH.sub.3 → 5N.sub.2 + 6H.sub.2 O

    6no.sub.2 + 8nh.sub.3 → 7n.sub.2 + 12h.sub.2 o

the reducing method using ammonia is called a selective reducing methodbecause nitrogen oxides react with ammonia selectively to some extenteven in the presence of oxygen. It has the advantage that theconsumption of ammonia by oxygen present in exhaust gases can beinhibited.

Known catalysts for use in the vapor-phase catalytic reduction ofnitrogen oxides of the above type include a catalyst comprising vanadiumoxide or molybdenum oxide supported on alumina or silica gel (U.S. Pat.No. 3,279,884), a catalyst comprising an oxide of a transition metal(excepting noble metals), such as copper oxide, iron oxide, chromiumoxide, cobalt oxide or nickel oxide, supported on alumina of a highsurface area (Japanese Laid-Open Patent Publication No. 75464/74), and acatalyst comprising an oxide of a transition metal (excepting noblemetals), such as vanadium oxide or cerium oxide, supported on titaniumoxide (Japanese Laid-Open Patent Publications Nos. 51996/75 and65467/75).

The catalyst comprising a transition metal oxide (excepting noble metaloxides), such as vanadium oxide, molybdenum oxide, copper oxide or ironoxide, supported on an ordinary carrier such as alumina or silica gelexhibits high catalytic activity in the early stage, but has the defectthat it cannot retain its activity stably over long periods of timebecause it is poisoned by sulfur oxides (mainly denoting SO₂ and SO₃ ;generically called "sulfur oxides" in the present application) which arenormally contained in nitrogen oxide-containing exhaust gases. Thecatalyst comprising a transition metal oxide (excepting noble metaloxides), such as vanadium oxide or cerium oxide, supported on titaniumoxide has good catalytic activity and good resistance to poisoning bysulfur oxides. On the other hand, it has poor moldability into thedesired shape, and poor physical strength with susceptibility todestruction by a physical destructive force exerted during its handlingor use. Because of the low physical strength, this catalyst is subjectto various troubles during use for long periods, and the restriction onits shape makes it difficult to reduce pressure drop and to maintain alow pressure drop for long periods of time.

The present inventors extensively worked in an attempt to provide acommercially satisfactory process for the catalytic vapor-phasereduction of nitrogen oxides and a catalyst composition for use in theprocess, which are free from the disadvantages and defects of theconventional catalysts described hereinabove. This led to the discoverythat a catalyst composition consisting essentially of a non-nobletransition metal compound supported on a shaped carrier comprisingtitanium oxide and a low-cost readily available clay mineral, preferablya clay mineral having an average particle size of 0.1 to 100 microns,retains high catalytic activity and superior resistance to poisoning inthe reduction of nitrogen oxides over long periods of time. It was alsofound that the catalyst composition can be molded into various desiredshapes, and has satisfactory physical strength sufficient forwithstanding physical destruction during its handling or use. Theinventors further found that these improvements can be enhanced byincluding an additional carrier component which is an inorganic fibrousmaterial, silica hydrogel, silica sol, or a mixture of at least two ofthese.

It has been found that according to the present invention, a process forthe catalytic vapor-phase reduction of nitrogen oxides and a catalystcomposition for use in it can be provided which achieve manyimprovements and advantages, such as high catalytic activity inreduction, superior resistance to poisoning, retention of theseproperties for long periods of time, superior moldability, high physicalstrength, the ability to permit the decrease of pressure drop during areducing operation, maintenance of a low pressure drop over long periodsof time, increased activity per unit weight of catalyst, the preventionof the masking of catalyst surface and blockage of the catalyst layerdue to dust present in waste gases to be treated, and continuedstability of treatment.

Accordingly, it is an object of this invention to provide a process forcatalytically reducing nitrogen oxides which can achieve markedimprovements.

Another object of this invention is to provide an improved catalystcomposition suitable for use in the above process.

The above and other objects and advantages of the present invention willbecome apparent from the following description.

The catalyst composition of this invention consists essentially of anon-noble transition metal compound supported on a shaped carriercomprising a titanium oxide and a clay mineral having an averageparticle size of 0.1 to 100 microns. Preferably, the catalystcomposition consists essentially of a non-noble transition metalcompound supported on a shaped carrier composed of a titanium oxide, aclay mineral having an average particle size of 0.1 to 100 microns, andan additional component which is an inorganic fibrous material, silicahydrogel, silica sol or a mixture of at least two of these species.

The term "non-noble transition metal", as used in the presentapplication, denotes transition metals excepting noble metals.

The titanium oxide used in the present invention is a term which denoteshydrous titanium oxides, such as ortho-titanic acid or meta-titanicacid, obtained by hydrolyzing titanium salts such as titanium chlorideor titanium sulfate, and titanium oxides obtained by drying thesehydrous titanium oxides at room temperature to 1,000° C. It includesoxides of titanium such as titanium (II) oxide (titanium monoxide, TiO),titanium (III) oxide (titanium sesquioxide, Ti₂ O₃), titanium (IV) oxide(titanium dioxide, TiO₂), ortho-titanic acid (α-titanic acid), andmeta-titanic acid (β-titanic acid), and mixtures of these.

Examples of the clay mineral used in the present invention aremontmorillonite-type clay minerals such as montmorillonite, bentonite,acid terra alba, activated clay or fuller's earth; kaolin-type clayminerals such as German kaolinite (occurring in west Germany),kibushi-clay (occurring in Aichi, Japan), Gaerome clay (occurring inAichi, Japan), Georgia kaolin, and kaolinite; halloysite-type clayminerals such as halloysite or hydrated halloysite; pyrophyllite-typeclay minerals such as agalmatolite or pyrophyllite; sericite-type clayminerals such as Murakami clay (occurring in Niigata, Japan); andmixtures of these clay minerals in optional combinations.

For good moldability and physical strength of the resulting catalystcomposition, the clay mineral preferably has an average particle size of0.1 to 100 microns.

The non-noble transition metal compound used in this invention includes,for example, the oxides or sulfates of metals selected from metals ofGroups IB, VIB, VB, VIIB and VIII of the periodic table and cerium.Oxides of metals selected from copper, vanadium, chromium, molybdenum,tungsten, manganese, iron and cerium are especially preferred. Thesecompounds can be used either alone or in admixture of two or more.

The oxidation number of the metal oxide is not restricted in particular,and oxides of any oxidation number are feasible. Specific examples ofsuitable non-noble transition metal compounds are vanadium pentoxide (V₂O₅), vanadium dioxide (VO₂), vanadium trioxide (V₂ O₃), cupric oxide(CuO), ferric oxide (Fe₂ O₃), ferroferric oxide (Fe₃ O₄), molybdenumtrioxide (MoO₃), tungsten dioxide (WO₂), and tungsten trioxide (WO₃).

A preferred catalyst composition of this invention comprises 0.1 to 20%by weight, preferably 0.5 to 15% by weight, of the non-noble transitionmetal compound, 1 to 60% by weight, preferably 5 to 20% by weight, ofthe clay mineral, and 20 to 90% by weight, preferably 70 to 90% byweight, of the titanium oxide, all proportions being based on the weightof the catalyst composition. In an especially preferred form of thecatalyst composition of this invention, the shaped carrier furtherincludes a component selected from an inorganic fibrous material, silicahydrogel, silica sol, and a mixture of at least two of these species.The amount of the additional carrier component is 0.5 to 25% by weightbased on the total weight of the titanium oxide and the clay mineral.

Suitable proportions of the ingredients of the catalyst composition ofthis invention are, for example, as follows:

    ______________________________________                                        Titanium oxide      60 to 95% by weight                                       Clay mineral         5 to 30% by weight                                       Additional carrier                                                            component            3 to 10% by weight                                       Non-noble transition                                                          metal compound       3 to 15% by weight                                       ______________________________________                                    

The inorganic fibrous material as the other carrier component may beinorganic fibrous materials of natural origin and artificial orsynthetic origin. Examples of the inorganic fibrous material are glasswool, glass fibers, rock wool, Kaowool (registered trademark), asbestos,and mixtures of at least two of these. Preferably, the inorganic fibrousmaterial has a fiber length of 0.01 to 200 mm and a fiber diameter ofnot more than about 1 mm. It is especially preferred that the fiberlength be at least about 10 times the fiber diameter.

The silica hydrogel or silica sol as the additional carrier component ispreferably in the form of fine particles having an average particle sizeof not more than 10 mμ, for example, 0.1 to 10 mμ, in order to increasethe thermal stability of the catalyst.

The silica hydrogel and silica sol, as used in the invention, contain atleast 50% by weight of a silica component, and may embrace a hydrogel orsol of silica-alumina or silica-magnesia containing at least 50% byweight of a silica component.

The catalyst composition of this invention should preferably be in theform of hollow cylinder. The catalyst composition of this inventionwhich includes the additional carrier component described above isespecially preferred for fabrication into a hollow cylindrical shapebecause it can be molded into any desired shape and has superiorphysical strength. The previously suggested catalysts consisting of anon-noble transition metal compound supported on a titanium oxidecarrier cannot be fabricated into such a shape because of its poormoldability and low physical strength, and catalysts feasible forpractical purposes cannot be obtained.

The cross-sectional shape of the hollow cylindrical carrier of thecatalyst composition of this invention is preferably circular or nearlycircular. Generally, the catalyst pellets have such a shape as willpermit minimization of the areas of contact between the pellets whenthey are packed in a reducing zone with their axes of cylinder alignedin one direction, namely such a shape as will allow sufficient spacesamong the cylindrical pellets, and for example, they may have apolygonal (e.g., heptagonal or more) cross-sectional shape. It should beunderstood that these shapes are also included within the term"cylindrical" as referred to in the present application.

It is especially preferred that the pellets of the catalyst compositionof this invention molded into a hollow cylindrical shape especiallypreferably have an inside diameter of 5 to 40 mm, especially 15 to 40mm, and an outside diameter-to-inside diameter ratio of from 1.2 to 1.6.The height of each cylinder is preferably at least about 100 mm, forexample, 100 to 3,000, more preferably 200 to 1,000 mm.

With conventional catalyst compositions used to reduce nitrogen oxideswith ammonia in the vapor phase, attempts are made to minimize theparticle diameter of the catalyst pellets in order to increase theapparent surface area of the catalyst composition per unit weightthereof. Thus, these catalyst compositions are generally used in theform of small spheres, tablets or cylindrical pellets each having adiameter and a height of 5 to 10 mm. When a catalyst of such a shape isused as packed in a fixed bed reactor, dust normally contained in afairly large amount in nitrogen oxide-containing waste gases tends tocause the masking of the catalyst surface or the blockage of thecatalyst-packed layer. In order to avoid these disadvantages, it hasbeen the previous practice to modify the reactor itself by usingcomplicated and expensive means in designing and production. Incontrast, the present invention can afford a catalyst composition havingsuperior catalytic activity and being of a cylindrical shape as a resultof marked improvement in moldability and physical strength. Theaforesaid masking or blocking troubles can be easily avoided just bypacking the catalyst composition into a reactor in such a manner thatthe axes of the hollow cylindrical pellets are aligned in the directionof gas flow. There is no need to subject the reactor to the complicatedand expensive modification.

The catalyst composition of this invention in the form of hollowcylindrical pellets of the suitable sizes described above is especiallypreferred because it conveniently avoids the aforementioned troubles,and exhibits superior catalytic activity and resistance to poisoningover long periods of time in addition to having a good efficiency ofcontact with gases and high physical strength, and permitting thedecrease of pressure drop.

The catalyst composition of this invention can be prepared, for example,by mixing an aqueous solution of a water-soluble salt of a non-nobletransition metal, such as nitrates, carbonates, oxalates or ammoniumsalts, the titanium oxide, and the clay mineral with or without theadditional carrier component described hereinabove, shaping the mixtureinto the desired shape (for example, by extrusion molding), drying themolded mixture, and calcining it. Alternatively, it can be prepared byfirst preparing a shaped carrier by kneading the titanium oxide and claymineral with or without the additional carrier component in the presenceof a small amount of water, molding the mixture into the desired shape(for example, by extrusion molding), drying the molded mixture andcalcining it; impregnating the shaped carrier with an aqueous solutionof the water-soluble salt of the transition metal; drying it at 20 to100° C. for 10 to 50 hours; and calcining the dried product. Calcinationcan be performed, for example, at a temperature of at least about 100°C., usually 300 to 700° C. In the catalyst preparing method described, adissolving or mixing aid such as monoethanolamine may be added at thetime of kneading the individual components of the catalyst or startingmaterials for these components.

The shape of the catalyst can be a sphere, tablet, cylinder, ring, orhoneycomb. Preferably, the catalyst composition, as stated hereinabove,is in the form of hollow cylindrical pellets having a fairly large size.

According to the present invention, there can be provided a process forthe catalytic vapor-phase reduction of nitrogen oxides contained in awaste gas, which comprises contacting said waste gas with a catalystcomposition in the presence of ammonia gas at a temperature of 200 to600° C., said catalyst composition consisting essentially of a non-nobletransition metal compound supported on a shaped carrier composed of atitanium oxide and a clay mineral having an average particle size of 0.1to 100 microns, preferably together with an additional carrier componentselected from the group consisting of an inorganic fibrous material,silica hydrogel, silica sol, and a mixture of at least two of thesespecies.

The catalytic vapor-phase reduction of the nitrogen oxide-containingwaste gas can be performed by introducing a gaseous mixture of it with0.5 to 5 moles, preferably 1 to 2 moles, per stoichiometrically requiredmole of the nitrogen oxides to be removed through a reaction zone packedwith the catalyst composition. Alternatively, this can be performed byintroducing the nitrogen oxide-containing waste gas and ammoniasimultaneously from separate openings through the catalyst layer. Any ofmoving bed, fluidized bed and fixed bed can be used in the reaction, butthe use of a fixed bed-system is preferred.

The reaction temperature somewhat differs according to the proportionsof the ingredients of the catalyst composition. The suitable reactiontemperature is generally 200 to 600° C., preferably 250 to 450° C.

When the reaction is carried out at a temperature exceeding 600° C.,part of ammonia as a reducing agent tends to react with oxygen presentin the exhaust gas to form nitrogen oxides. On the other hand, if thereaction temperature is lower than 200° C., there is a tendency to theformation of ammonium nitrate or ammonium nitrite, and in the presenceof SO₂, sulfates or sulfites tends to be formed, or NO and NO₂ cannot bereduced to nitrogen and nitrogen suboxide (N₂ O) is formed as aby-product. Hence, temperatures outside the specified range areundesirable.

The reaction time, which is expressed in terms of space velocity,differs according to the proportions of the catalyst ingredients.Usually, the space velocity is 1,000 to 100,000 Nm³, preferably 5,000 to30,000 Nm³, per hour per m³ of catalyst.

The reaction pressure may be atmospheric, reduced or elevated pressures.

In a preferred embodiment of the present invention in which hollowcylindrical catalyst pellets are used, it is preferred to arrange thecatalyst pellets regularly in a catalytic reaction zone so that the axesof the hollow cylindrical pellets correspond substantially with thedirection of the flow of the feed gas in the reaction zone.Specifically, the catalyst pellets may be arranged in a square shape ordiamond shape, etc. In this manner of arrangement, it is desirable tostack the catalyst pellets coaxially to a suitable thickness. As aresult, not only the inside surfaces of the hollow portions of thecatalyst pellets, but also their outside surfaces can be effectivelyutilized. The packing of the hollow cylindrical catalyst pellets can beperformed by a close contact method in which they are arranged so thattheir outside surfaces contact one another partly, or by a sparsepacking method in which they are arranged with suitable spaces alongthem to avoid contact. The latter method of arrangement can bepractised, for example, by extending lead wires within a reactor tosupport the catalyst pellets properly; or by supporting them by anyother suitable supports.

According to the process of this invention, a high ratio of nitrogenoxide removal can be maintained for very long periods of time even whenreducing nitrogen oxides in a waste gas, such as a boiler exhaust gas,consisting of 100 to 1,000 ppm of nitrogen oxides (mainly NO), 200 to2,000 ppm of sulfur oxides (mainly SO₂), 1 to 8% by volume of oxygen, 5to 20% by volume of CO₂, and 5 to 20% by volume of steam in the presenceof ammonia. In the treatment of waste gases containing large quantitiesof dusts, for example, boiler exhaust gases, the use of hollowcylindrical catalysts of this invention can advantageously avoid maskingor blocking of the catalyst layer, and the catalysts can be used overlong periods of time. Hence, the present invention is of greatcommercial significance.

The following examples illustrate the present invention in greaterdetail. It should be understood that the invention is not limited tothese examples.

The mechanical strength of the catalyst is expressed in terms ofpressure resistant strength which is measured by the following method.The catalyst is compression-molded (compression ratio 24) intocylindrical pellets each having a diameter of 5 mm and a height of 3.8mm. The destruction strength of each of the cylindrical pellets ismeasured by a Kiya-type hardness tester. When the catalyst is in theform of hollow cylindrical pellets, they are cut so that the length ofeach pellet in the direction of its hollow axis equals the outsidediameter of its cross-section, and the destruction strength of eachhollow cylindrical catalyst pellet in its diametrical direction ismeasured by a Kiya-type hardness tester.

EXAMPLES 1 TO 10 AND COMPARATIVE EXAMPLES 1 TO 13

A mixture of 93.6 g of titanium oxide and active clay having a particlediameter of 0.1 to 10 microns was thoroughly kneaded with 80 ml of anaqueous solution containing 15 g of ammonium metavanadate and 13 g ofmonoethanolamine, and the mixture was extrusion molded into cylindricalpellets having a diameter of 5 mm and a height of 5 mm. The pellets weredried, and then calcined in air at 500° C. for 3 hours within a mufflefurnace. Thus, a catalyst consisting of 10% by weight, as V₂ O₅, ofvanadium, 10% by weight of active clay and 90% by weight of TiO₂ wasprepared. The pressure resistant strength of this catalyst was measured,and the results are shown in Table 1 below.

The catalyst so prepared was packed in an amount of 2 liters into areaction tube having an inside diameter of 10 cm and a height of 50 cm,and a mixture consisting of 300 ppm of ammonia and a gas simulating atypical boiler exhaust gas, i.e. a gas consisting of 300 ppm of NO, 300ppm of SO₂, 15% by volume of CO₂, 12% by volume of H₂ O, and theremainder being N₂, was passed through the catalyst layer at atemperature of 350° C. and a space velocity of 30,000 hr⁻¹. The NOremoval ratio at this time is shown in Table 1. The NO removal ratio wasalso determined after continuing this reactiobn for 500 hours, and theresults are also shown in Table 1.

Various catalyst compositions were prepared in the same manner asdescribed above except that the active catalyst ingredient and the claymineral were changed as indicated in Table 1. The proportions of thecatalyst ingredients, the pressure resistant strengths of the catalysts,and the NO removal ratios of these catalysts in the same reaction asabove are shown in Table 1.

Table 1 also shows the results of comparative tests in which the claymineral was not used, and those in which a γ-alumina or silica hydrogelcarrier was used instead of TiO₂.

                                      Table 1                                     __________________________________________________________________________    Example                                       NO removal ratio                (EX.) or                                                                             Composition of catalyst (% by weight)                                                                           Strength                                                                           (%)                             Comparative                                                                          Active         Clay mineral       of the    After                      Example                                                                              ingredient                                                                             TiO.sub.2        Size    catalyst  500                        (CE.)  Type wt. %                                                                             wt. % Type       (μ)                                                                            wt. %                                                                             (kg) Initial                                                                            hours                      __________________________________________________________________________    EX. 1  V.sub.2 O.sub.5                                                                    10  80    Active clay                                                                              0.1-10                                                                            10  18.8 91   91                         CE. 1  V.sub.2 O.sub.5                                                                    10  90    --         --  --  3.3  90   88                         EX. 2  V.sub.2 O.sub.5                                                                    10  74    Bentonite  0.1-10                                                                            15  9.5  90   89                         CE. 2   "   10  90    --         --  --  3.3  90   88                         EX. 3  Cr.sub.2 O.sub.3                                                                    7  83    Acid terra alba                                                                          0.1-10                                                                            10  11.7 91   87                         CE. 3   "   10  90    --         --  --  3.2  90   85                         EX. 4  Fe.sub.2 O.sub.3                                                                   10  40    Active clay                                                                              0.1- 10                                                                           50  28.6 88   83                         CE. 4   "   10  90    --         --  --  3.8  87   82                         EX. 5  Fe.sub.2 O.sub.3                                                                    5  85    Kaolin     0.2-20                                                                            10  10.1 89   87                         CE. 5   "   10  90    --         --  --  3.8  87   82                         EX. 6  MoO.sub.3                                                                          15  80    Montmorillonite                                                                          0.1-3                                                                              5  9.0  88   87                         CE. 6   "   10  90    --         --  --  3.1  88   85                         EX. 7  CeO  10  70    Bentonite  0.1-10                                                                            20  14.3 88   86                         CE. 7   "   10  90    --         --  --  3.6  88   84                         Ex. 8  V.sub.2 O.sub.5                                                                    10  75    Kaolin     0.1-2                                                                             15  22.5 91   89                                               (occurring in Shipaha)                                  CE. 8   "   10  90    --         --  --  3.3  90   88                         EX. 9  V.sub.2 O.sub.5                                                                     8  72    Kaolin     0.1-2                                                                             15  27.8 90   89                                               (occurring in Shipaha)                                                        Gaerome clay                                                                             5-100                                                                              5                                       CE. 9   "   10  90    --         --  --  3.3  90   88                         EX. 10 V.sub.2 O.sub.5                                                                    10  75    Active clay                                                                              0.1-10                                                                            15  19.5 91   91                         CE. 10  "   10  γ-alumina                                                                     --         --  --  15.2 52   31                                         90                                                                            Silica                                                        CE. 11  "   10  hydrogel                                                                            --         --  --  1.6  13   12                                         90                                                            CE. 12  "   10  90    --         --  --  3.3  90   88                                         γ-alumina                                                               (60)                                                          CE. 13  "   10  TiO.sub.2                                                                           --         --  --  8.4  74   67                                         (30)                                                          __________________________________________________________________________

EXAMPLE 11

A 100-liter stainless steel kneader equipped with a steam jacket wascharged with 60 kg of meta-titanic acid containing 30% of titaniumoxide, and with stirring, the pH of the material was adjusted to 8.5with a 15% aqueous solution of ammonia.

Separately, 2.75 kg of ammonium meatvanadate was dissolved in 25 kg ofhot water to form a solution having a concentration of about 10%.

The neutralized metal-titanic acid was stirred, and mixed with ammoniummetavanadate. Then, 3.75 kg of kaolin having a particle size of 0.1 to 2microns (occurring in Shipaha) and 1.25 kg of glass fibers (NittoboGlass Fiber Chopped Strands, CS-3E-221) were added, and sufficientlymixed with the solution. The resulting slurry was heated, masticated,concentrated to a water content suitable for fabrication, and thenmolded by an extruder into pellets having a diameter of 5.0 mm and alength of 5.0 to 6.0 mm.

The pellets were dried overnight at 110° C., and calcined in the air at400° C. for 3 hours. The pressure resistant strength of the catalyst andits NO removal ratio in the same reaction as in Example 1 weredetermined, and the results are shown in Table 2. Table 2 also containsthe data for Example 9 for easy reference.

                                      Table 2                                     __________________________________________________________________________                             Example 9                                                                            Example 11                                    __________________________________________________________________________           Active  Type      V.sub.2 O.sub.5                                                                      V.sub.2 O.sub.5                                      ingredients                                                                          % by weight                                                                               8      8                                                   TiO.sub.2 (wt. %) 72     72                                                                     Kaolin Kaolin                                                      Type       occurring                                                                            occurring                                            Clay (A)          in Shipaha                                                                           in Shipaha                                                  Particle size (μ)                                                                     0.1-2  0.1-2                                         Catalyst      % by weight                                                                              15     15                                            ingredients   Type       Gaeorome                                                                             --                                                                     clay                                                        Clay (B)                                                                             Particle size (μ)                                                                     5-100  --                                                          % by weight                                                                               5     --                                                    Glass fibers (% by weight)                                                                     --      5                                            Pressure resistant strength (kg)                                                                        27.8   35.4                                         NO removal                                                                            Initial          90     90                                            ratio                                                                          (%)   After 500 hours   89     90                                            __________________________________________________________________________

EXAMPLES 12 AND 13 AND COMPARATIVE EXAMPLES 13 TO 14

A 100-liter stainless steel kneader equipped with a steam jacket wascharged with 60 kg of meta-titanic acid containing 30% of titaniumoxide, and with stirring, the pH of the material was adjusted to 8.5with a 15% aqueous solution of ammonia.

Separately, 2.75 kg of ammonium metavanadate was dissolved in 25 kg ofhot water to form a solution having a concentration of about 10%.

The neutralized metal-titanic acid was stirred and mixed with ammoniummetavanadate. Then, 3.75 kg of kaolin occurring in Shipaha and having aparticle diameter of 0.1 to 2 microns and 1.25 kg of glass fibers (Glassfiber chopped strands, CS-3E-221; a product of Nittobo, Japan) wereadded to the mixture, and they were thoroughly mixed. The slurry washeated, masticated, and concentrated to water content suitable formolding. The mixture was then molded by an extruder into hollowcylindrical pellets each having an outside diameter of 33.0 mm, aninside diameter of 23.0 mm and a height of 300 mm. The strength of thiscatalyst was measured by the method described hereinabove, and itsstrength in the diametrical direction is shown in Table 3.

Eighty-one cylindrical catalyst pellets obtained were packed into areactor in a square shape in intimate contact with one another, andstacked concentrically to a height of 2.7 m (9 layers). A gaseousmixture of a boiler exhaust gas composed of 230 ppm of NO, 800 ppm ofSO₂, 12% by volume of CO₂, 10% by volume of H₂ O and the remainder beingN₂ and containing 150 mg/Nm³ dry of dust with 230 ppm of ammonia waspassed into the reactor at a space velocity of 5,000 hr⁻¹ and atemperature of 350° C.

The NO removal, the liquid velocity (L.V.) and the pressure drop at thistime are shown in Table 3.

For comparison, a V₂ O₅ -TiO₂ -glass fiber catalyst was prepared by thesame method as in the preparation of catalyst in Example 13 except thatthe clay was not used. The catalyst was molded into hollow cylindricalpellets each having an inside diameter of 23 mm, an outside diameter of33 mm, and a height of 300 mm. These cylindrical pellets were packedclosely in a reactor in the same way as in Example 13, and quite thesame reaction as in Example 13 was performed. The strength of the hollowcylindrical catalyst, the NO removal ratio, the liquid velocity (L.V.),and the pressure drop are shown in Table 3.

                                      Table 3                                     __________________________________________________________________________    Example                             NO removal                                                                             Pressure drop                    (EX.) or                                                                             Catalyst ingredients                                                                        Strength       ratio (%)                                                                              (mm Aq)                          Comparative                                                                          (% by weight) of catalyst         After    After                       Example          Glass                                                                             (diameter)                                                                          L.V. S.V.     500      500                         (CE.)  V.sub.2 O.sub.5                                                                   TiO.sub.2                                                                        Clay                                                                             fiber                                                                             (kg)  (m/sec.)                                                                           (hr.sup.-1)                                                                       Initial                                                                            hours                                                                             Initial                                                                            hours                       __________________________________________________________________________    Ex. 12 8   72 15 5   10    86   5,000                                                                             92   92  80   80                          CE. 13 9   81  0 10  4     86   5,000                                                                             92   92  80   80                          Ex. 13 8   77 15 0   6     86   5,000                                                                             92   92  80   80                          CE. 14 8   92  0 0   1     86   5,000                                                                             91   89  80   100                         __________________________________________________________________________

EXAMPLES 14 AND 15

The procedure of Example 12 was repeated except that the composition ofthe catalyst was changed as shown in Table 4. The results obtained areshown in Table 4.

EXAMPLE 16

A catalyst was prepared in the same way as in Example 12 except that ahydrogen containing silica with a size of 2.51 mμ was further added asan additional carrier component. Using this catalyst, the same reactionas in Example 12 was performed except that the reaction temperature waschanged to 420° C. The results are shown in Table 4.

                                      Table 4                                     __________________________________________________________________________    Composition of the catalyst  (% by weight)                                    Type and                                              NO removal ratio        amount      Amount               Additional           (%)                     (wt. %) of  of   Clay mineral    carrier component                                                                           Strength    After                   active in-                                                                           TiO.sub.2                                                                          Type and amount                                                                          Size Type and amount                                                                         Size                                                                              of Catalyst 500                Example                                                                            gredient                                                                             (wt. %)                                                                            (wt. %)    (μ)                                                                             (wt. %)   (mμ)                                                                           (kg)   Initial                                                                            hours              __________________________________________________________________________    14   V.sub.2 O.sub.5  (8)                                                                 72   Kaolin occurring                                                                         0.1-2                                                                              Asbestos  --  9.5    91   91                                  in Shipaha      (5)                                                           (15)                                                         15   V.sub.2 O.sub.5  (8)                                                                 72   Kaolin occurring                                                                         0.1-2                                                                              Rock wool*                                                                              --  9.5    91   91                                  in Shipaha      (5)                                                           (15)                                                                          Active clay     Silica    2.51                               16   V.sub.2 O.sub.5  (10)                                                                60   (15)        0.1-10                                                                            (10)          8.5    92   92                                                  Glass Fibers                                                                            --                                                                  (5)                                          __________________________________________________________________________     *ROCK FIBER 42, a product of Nittobo Co., Ltd.                           

What is claimed is:
 1. A catalyst composition for use in the vapor phasereduction of nitrogen oxides with ammonia, said catalyst compositionconsisting essentially of a non-noble transition metal compoundsupported on a shaped carrier comprising a titanium oxide, a claymineral having an average particle size of 0.1 to 100 microns and anadditional component which is an inorganic fibrous material or a mixtureof the fibrous material and at least one member selected from the groupconsisting of silica hydrogel and silica sol, wherein the clay mineralis selected from the group consisting of montmorillonite clay minerals,kaoline clay minerals, halloysite clay minerals, pyrophyllite clayminerals and sericite clay minerals and the catalyst compositioncontains 0.1 to 20% by weight of the non-noble transition metalcompound, 1 to 60% by weight of the clay mineral, and 20 to 90% byweight of the titanium oxide, all based on the weight of the catalystcomposition and 0.5 to 25% by weight of the additional component basedon the total weight of the titanium oxide and clay mineral.
 2. Thecatalyst composition of claim 1 wherein the non-noble transition metalcompound is an oxide or sulfate of a metal selected from the groupconsisting of metals of Groups IB, VIB, VB, VIIB and VIII of theperiodic table and cerium.
 3. The catalyst composition of claim 1wherein the non-noble transition metal compound is an oxide of a metalselected from the group consisting of copper, vanadium, chromium,molybdenum, tungsten, manganese, iron and cerium.
 4. The catalystcomposition of claim 1 wherein the inorganic fibrous material isselected from the group consisting of glass wool, glass fiber, rockwool, Kaowool and asbestos.
 5. The catalyst composition of claim 1wherein the additional component is the mixture of the fibrous materialand at least one member selected from the group consisting of silicahydrogel and silica sol wherein the silica hydrogel and the silica solhave an average particle size of 0.1 to 10 mμ.
 6. The catalystcomposition of claim 5 wherein the silica hydrogel and silica sol eachcontain at least 50% by weight of a silica component.
 7. The catalystcomposition of claim 1 wherein the clay mineral is selected from thegroup consisting of montmorillonite, bentonite, acid terra alba,activated clay, fuller's earth, German kaolinite, kibushi-clay, Gaeromeclay, Georgia kaolin, halloysite, hydrated halloysite, agalmatolite,pyrophyllite, and Murakami clay or mixtures thereof.
 8. The catalystcomposition of claim 1 wherein the non-noble transition metal compoundis selected from the group consisting of vanadium pentoxide, vanadiumdioxide, vanadium trioxide, cupric oxide, ferric oxide, ferroferricoxide, molybdenum, trioxide, tungsten dioxide, and tungsten trioxide. 9.The catalyst composition of claim 1 having the following proportions ofthe ingredients:

    ______________________________________                                        Titanium oxide      60 to 90% by weight                                       Clay mineral         5 to 30% by weight                                       Additional component                                                                               3 to 10% by weight                                       Non-noble transition                                                          metal compound       3 to 15% by weight.                                      ______________________________________                                    


10. The catalyst composition of claim 1 wherein the additional componentis the inorganic fibrous material which is selected from the groupconsisting of glass wool, glass fiber, rock wool, Kaowool and asbestos.11. The catalyst composition of claim 10 wherein the inorganic fibrousmaterial has a fiber length of 0.01 to 200 mm and a fiber diameter ofnot more than about 1 mm.
 12. The catalyst composition of claim 11wherein the ratio of the length to diameter of the inorganic fibrousmaterial is at least about 10:1.
 13. The catalyst composition of claim 1which is in the form of hollow cylindrical pellets.
 14. The catalystcomposition of claim 13 wherein each hollow cylindrical pellet has aninside diameter of 5 to 40 mm, and the ratio of its outside diameter toits inside diameter is from 1.2 to 1.6.
 15. The catalyst composition ofclaim 14 wherein each hollow cylindrical pellet has an inside diameterof 15 to 40 mm.
 16. The catalyst composition of claim 15 wherein theheight of each hollow cylinder is between from about 100 to 3,000 mm.17. The catalyst composition of claim 15 wherein the height of eachhollow cylinder is from about 200 to 1,000 mm.